Carbon steel for cutlery - 80CRV2 / 1.2235 / L2 - Eurotechni

Carbon steel for cutlery - 80CRV2 / 1.2235 / L2 - Eurotechni - Top

80CRV2 / 1.2235 / L2

80CrV2 multi-use steel used to make blades for cutting tools and instruments. Characteristics of 80CrV2 steel: The 80CrV2 carbon steel is a low alloy steel that has better tensile strength and quench properties than non-alloyed carbon steels. It is a relatively high carbon content, an...

More information

Dimensions	Stock	Price	Quantity
Total		0 €
82 x 4 x 910 mm	En stock	€27.00 €22.50 Excl. Tax	Out of stock
99 x 2,8 x 1000 mm	En stock	€20.50 €17.08 Excl. Tax	17.080000
80 x 3.3 x 710 mm	En stock	€23.00 €19.17 Excl. Tax	19.170000
80 x 4 x 710 mm	En stock	€22.00 €18.33 Excl. Tax	18.330000
80 x 5,3 x 860 mm	En stock	€32.50 €27.08 Excl. Tax	27.080000
80 x 6.2 x 610 mm	En stock	€36.00 €30.00 Excl. Tax	30.000000
80 x 7,3 x 820 mm	En stock	€40.50 €33.75 Excl. Tax	33.750000

Technical sheet

Customer reviews

dimension

Further information

Shape	Flat
Use	Blade
Sub-category	Standard
Carbon	0.8 %
Chromium	0.5 %
Manganese	0.4 %
Silicium	0.25 %
Vanadium	0.2 %

DIMENSIONS

Thickness	4 mm
Length	910 mm
Width	82 mm

heat treatment

Hardness after tempering	60 (HRC)
Quenching temperature	830 C°

denominations

Wnr	1.2235
AISI	L2
AFNOR	80CrV2

Further information

Carbon	0.8 %
Chromium	0.5 %
Manganese	0.4 %
Silicium	0.25 %
Vanadium	0.2 %

DIMENSIONS

Thickness	2.8 mm
Length	1000 mm
Width	99 mm

heat treatment

Hardness after tempering	60 (HRC)
Quenching temperature	830 C°

denominations

Wnr	1.2235
AISI	L2
AFNOR	80CrV2

Further information

Carbon	0.8 %
Chromium	0.5 %
Manganese	0.4 %
Silicium	0.25 %
Vanadium	0.2 %

DIMENSIONS

Thickness	3.3 mm
Length	710 mm
Width	80 mm

heat treatment

Hardness after tempering	60 (HRC)
Quenching temperature	830 C°

denominations

Wnr	1.2235
AISI	L2
AFNOR	80CrV2

Further information

Shape	Flat
Use	Blade
Sub-category	Standard
Carbon	0.8 %
Chromium	0.5 %
Manganese	0.4 %
Silicium	0.25 %
Vanadium	0.2 %

DIMENSIONS

Thickness	4 mm
Length	710 mm
Width	80 mm

heat treatment

Hardness after tempering	60 (HRC)
Quenching temperature	830 C°

denominations

Wnr	1.2235
AISI	L2
AFNOR	80CrV2

Further information

Carbon	0.8 %
Chromium	0.5 %
Manganese	0.4 %
Silicium	0.25 %
Vanadium	0.2 %

DIMENSIONS

Thickness	5.3 mm
Length	860 mm
Width	80 mm

heat treatment

Hardness after tempering	60 (HRC)
Quenching temperature	830 C°

denominations

Wnr	1.2235
AISI	L2
AFNOR	80CrV2

Further information

Shape	Flat
Use	Blade
Sub-category	Standard
Food contact	Yes
Carbon	0.8 %
Chromium	0.5 %
Manganese	0.4 %
Silicium	0.25 %
Vanadium	0.2 %

DIMENSIONS

Thickness	6.2 mm
Length	610 mm
Width	80 mm

heat treatment

Hardness after tempering	60 (HRC)
Quenching temperature	830 C°

denominations

Wnr	1.2235
AISI	L2
AFNOR	80CrV2

Further information

Carbon	0.8 %
Chromium	0.5 %
Manganese	0.4 %
Silicium	0.25 %
Vanadium	0.2 %

DIMENSIONS

Thickness	7.3 mm
Length	820 mm
Width	80 mm

heat treatment

Hardness after tempering	60 (HRC)
Quenching temperature	830 C°

denominations

Wnr	1.2235
AISI	L2
AFNOR	80CrV2

Download the technical sheet

80CrV2 multi-use steel used to make blades for cutting tools and instruments.

Characteristics of 80CrV2 steel:

The 80CrV2 carbon steel is a low alloy steel that has better tensile strength and quench properties than non-alloyed carbon steels. It is a relatively high carbon content, and can reach good hardness levels. It is commonly used to make blades subjected to difficult working conditions: hand saws, shears or pruning shears for its resilience and capacity to resist shocks.

Ideal for outdoor and utility blades

Widely preferred for making scissors blades, it is a grade that is suited for making outdoor or utility carbon blades. It is often used in northern Europe to make Puukos, a popular utility knife that is simple and robust.
80CrV2 steel is hot rolled and is delivered annealed.
Find all of the information you need on 80CrV2 steel in its technical data file.